Product Description
Steel Wire Rod for Cold Drawing Nail Making (SAE1006 SAE1008)
Product description
Processing Technic: Hot Rolled Grade: SAE1006 SAE1008 SAE1010 SAE1012 GBQ195 Q235
Coil Weight: about 2 metric tons/coil
Size: 5.5mm,6.5mm,7.0mm,8.0mm,9.0mm,10.mm,11.0mm,12.0mm
Application
a).uesed for construction of reinforced concrete structure for reinforcement
b).used for nail making
c).used for construction as binding wire
d).uesd for tie wire and baling wire
e).used for making for wire mesh
Product No. 1: High Speed Hot rolled low carbon steel wire rods
| Grade | Application | Size(mm) | Standard | Delivery Status | Notes |
| Q195 | Mainly used for wire drawing and other general purpose. Applicable to the construction, drawing wires and other general purpose. | Φ5.5-Φ16.0 | GB/T701-2008 | Hot Rolled | Wire Rod Unit weight about 2000Kg |
| Q215 | Φ5.5-Φ16.0 | GB/T701-2008 | Hot Rolled | ||
| Q235 | Φ5.5-Φ16.0 | GB/T701-2008 | Hot Rolled | ||
| HPB235 | For the concrete structure engineering. | Φ6.5-Φ16.0 | GB/T1499.1-2008 | Hot Rolled |
Product No. 2: High Speed Hot rolled Carbon structural steel wire rods
| Grade | Application | Size(mm) | Standard | Delivery Status | Notes |
| 1006B 1008B 1012B 1017B 1018B | Mainly used for wire drawing, cold drawn or cold rolled steel wires. | Φ5.5-Φ16.0 | ASTM A510M & SAE Grade was used here. | Hot Rolled | Products of the other grades and chemical composition, specified in the contract by the supplier and demander, can be supplied. |
Product No. 3: High Speed Hot rolled low alloy steel wire rods
| Grade | Application | Size(mm) | Standard | Delivery Status | Notes |
| HPB300 | For the concrete structure engineering. | Φ5.5-Φ16.0 | GB/T1499.1-2008 | Hot Rolled | Wire Rod Unit weight about 2000Kg. 120t converter, refining furnace, protective casting. |
| HRB400 | Φ5.5-Φ16.0 | GB/T1499.2-2008 | Hot Rolled | ||
| HRB400E | Φ5.5-Φ16.0 | GB/T1499.2-2008 | Hot Rolled | ||
| 30MnSi | For the application of port concrete pipe pile, high buildings concrete pipe pile foundation, and the concrete pier pipe pile. | Φ5.5-Φ16.0 | GB/T24587-2009 | Hot Rolled |
Chemical Composition & Mechanical Properties
| chemical Composition | Mechanical Properties | ||||||||
| Grade | C | Mn | Si(≤) | P(≤) | S(≤) | B | Y.S.(Mpa) | T.S.(Mpa) | Elongation(%) |
| Q195 | 0.06-0.12 | 0.25-0.50 | 0.3 | 0.05 | 0.05 | 0.0008 | ≥195 | 315-430 | 33 |
| Q235 | 0.12-0.20 | 0.30-0.70 | 0.3 | 0.05 | 0.05 | 0.0008 | ≥235 | 375-500 | 26 |
| SAE1006 | ≤0.08 | 0.25-0.40 | 0.3 | 0.05 | 0.04 | 0.0008 | ≥210 | 210-370 | 32 |
| SAE1008 | ≤0.10 | 0.30-0.50 | 0.3 | 0.05 | 0.04 | 0.0008 | ≥195 | 315-430 | 30 |